Byenveni nan sit entènèt nou an!
Pri konpetitif rezistan FeCrAl fil enèji-efikas pri konpetitif Customize gwosè Solisyon chofaj endistriyèl
Pèfòmans Nomenklati alyaj
1Cr13AL4
0Cr25Al5
0Cr21AL6
0Cr23Al5
0Cr21Al4
0Cr21Al6Nb
0Cr27Al7Mo2
Prensipal konpozisyon chimik
Cr
12.0-15.0
23.0-26.0
19.0-22.0
20.5-23.5
18.0-21.0
21.0-23.0
26.5-27.8
Al
4.0-6.0
4.5-6.5
5.0-7.0
4.2-5.3
3.0-4.2
5.0-7.0
6.0-7.0
Re
apwopriye
apwopriye
apwopriye
apwopriye
apwopriye
apwopriye
apwopriye
Fe
Repoze
Repoze
Repoze
Repoze
Repoze
Repoze
Repoze
Nb0.5
Mo1.8-2.2
Max. Tanperati sèvis kontinyèl. nan eleman
(°C)
950
1250
1250
1250
1100
1350
1400
Rezistans nan 20ºC
(μΩ·m)
1.25
1.42
1.42
1.35
1.23
1.45
1.53
Dansite
(g/cm3)
7.4
7.1
7.16
7.25
7.35
7.1
7.1
Konduktivite tèmik (KJ/m·h·ºC)
52.7
46.1
63.2
60.2
46.9
46.1
–
Koefisyan ekspansyon liy yo
(α×10-6/ºC)
15.4
16
14.7
15
13.5
16
16
Pwen fizyon approx. (ºC)
1450
1500
1500
1500
1500
1510
1520
Fòs rupture
(N/mm2)
580-680
630-780
630-780
630-780
600-700
650-800
680-830
Elongasyon nan rupture (%)
> 16
> 12
> 12
> 12
> 12
> 12
> 10
Varyasyon nan zòn (%)
65-75
60-75
65-75
65-75
65-75
65-75
65-75
Repete frekans koube (F/R)
> 5
> 5
> 5
> 5
> 5
> 5
> 5
Dite (HB)
200-260
200-260
200-260
200-260
200-260
200-260
200-260
tan sèvis kontinyèl (èdtan / ºC)
–
≥80/1300
≥80/1300
≥80/1300
≥80/1250
≥50/1350
≥50/1350
Mikrografi estrikti
Ferit
Ferit
Ferit
Ferit
Ferit
Ferit
Ferit
Pwopriyete mayetik
Mayetik
Mayetik
Mayetik
Mayetik
Mayetik
Mayetik
Mayetik
Ekri mesaj ou la a epi voye l ba nou