Aws A5.14 nikèl alyaj Ernicu-7 MIG soude fil TIG soude baton pou Monel 400 soude
1. FM60 Oxford Alloy 60ERNiCu-7TIG baton soude
ERNiCu-7gen bon fòs ak reziste korozyon nan anpil medya, ki gen ladan dlo lanmè, sèl, ak diminye asid.Epi li ka itilize pou kouvri asye kabòn, bay yon kouch tanpon nan ERNi-1 yo itilize pou premye kouch la.Sa a alyaj se pa laj hardnable ak lè yo itilize yo rantre nan Monel K-500 gen pi ba fòs pase metal la baz.
Non komen: Oxford Alloy® 60 FM 60 Techalloy 418
Estanda: AWS 5.14 Klas ERNiCu-7 / ASME SFA 5.14 Klas ERNiCu-7 ASME II, SFA-5.14 UNS N04060 Werkstoff Nr.2.4377 ISO SNi4060 Ewòp NiCu30Mn3Ti
KONPOZISYON CHIMIK (%)
| C | Si | Mn | S | P | Ni |
| ≤0.15 | ≤1.25 | ≤4.0 | ≤0.015 | ≤0.02 | 62-69 |
| Al | Ti | Fe | Cu | lòt moun | |
| ≤1.25 | 1.5-3.0 | ≤2.5 | Repoze | <0.5 |
Paramèt soude
| Pwosesis | Dyamèt | Voltage | Anperaj | Gaz |
| TIG | .035″ (0.9mm) .045″ (1.2mm) 1/16″ (1.6mm) 3/32″ (2.4mm) 1/8″ (3.2mm) | 12-15 13-16 14-18 15-20 15-20 | 60-90 80-110 90-130 120-175 150-220 | 100% Agon 100% Agon 100% Agon 100% Agon 100% Agon |
| MIG | .035″ (0.9mm) .045″ (1.2mm) 1/16″ (1.6mm) | 26-29 28-32 29-33 | 150-190 180-220 200-250 | 75% Agon + 25% Elyòm 75% Agon + 25% Elyòm 75% Agon + 25% Elyòm |
| SAW | 3/32″ (2.4mm) 1/8″ (3.2mm) 5/32″ (4.0mm) | 28-30 29-32 30-33 | 275-350 350-450 400-550 | Yo ka itilize Flux apwopriye Yo ka itilize Flux apwopriye Yo ka itilize Flux apwopriye |
PWOPRIYETE MEKANIK
| Fòs rupture | 76,5000 PSI | 530 MPA |
| Sede fòs | 52,500 PSI | 360 MPA |
| Elongasyon | 34% |
APLIKASYON
ERNiCu-7 ka itilize pou aplikasyon soude diferan lè l sèvi avèk divès kalite alyaj nikèl-kwiv nikèl 200 ak alyaj kwiv-nikèl.
ERNiCu-7 yo itilize pou gaz-tengstèn-arc, gaz-metal-arc, ak submerged-arc soude nan alyaj Monel 400 ak K-500.
ERNiCu-7 se lajman ki itilize nan aplikasyon maren paske nan bon rezistans li yo nan efè yo korozivite nan dlo lanmè ak dlo salmè.