Constantan plat fil kwiv Nikèl alyaj 6j40 riban 0.4 * 2mm
Nouvo Constantan plat fil kwiv nikèl alyaj 6j11 riban 0.4 * 2mm
| Karakteristik | Rezistans (200C μ Ω. m) | Max. Tanperati travay (0C) | Fòs rupture (Mpa) | Pwen fizyon (0C) | Dansite (g/cm3) | TCR x10-6/ 0C (20 ~ 600 0C) | EMF vs Cu (μ V/ 0C) (0 ~ 100 0C) |
| Nomenklati alyaj | |||||||
| NC003 (CuNi1) | 0.1 | 200 | ≥ 250 | 1095 | 8.9 | <100 | -12 |
| Pwopriyete Fizik | Metrik | Kòmantè |
| Dansite | 8.94 g/cc | |
| Pwopriyete mekanik | Metrik | Kòmantè |
| Fòs rupture, ultim | 262 - 531 MPa | |
| Fòs rupture, Sede | 276 - 524 MPa | Tou depan de tanperaman |
| Allongement nan Break | 46.0% | nan 50.8 mm. |
| Modil Elastisite | 115 GPa | |
| Poissons rapò | 0.310 | Kalkile |
| Machinability | 20% | UNS C36000 (koupe gratis an kwiv) = 100% |
| Chea modil | 44.0 GPa | |
| Pwopriyete elektrik | Metrik | Kòmantè |
| Rezistivite elektrik | 0.0000120 ohm-cm @ Tanperati 20.0 ° C | |
| Pwopriyete tèmik | Metrik | Kòmantè |
| CTE, lineyè | 17.5 µm/m-°C @ Tanperati 20.0 - 300 ° C | |
| Kapasite Chalè Espesifik | 0.380 J/g-°C | |
| Kondiktivite tèmik | 64.0 W/mK @ Tanperati 20.0 ° C | |
| Pwen k ap fonn | < = 1125 ° C | Likid |
| Likid | 1125 ° C | |
| Pwopriyete Pwosesis | Metrik | Kòmantè |
| Tanperati Recuit | 565 - 815 ° C | |
| Tanperati cho-travay | 815 - 950 ° C | |
| Pwopriyete eleman eleman yo | Metrik | Kòmantè |
| Kwiv, Cu | > = 91.2% | |
| Iron, Fe | 1.30 - 1.70% | |
| Plon, Pb | < = 0.050% | |
| Manganèz, Mn | 0.30 - 0.80% | |
| Nikèl, Ni | 4.80 - 6.20% | |
| Zenk, Zn | < = 1.0% |
Kontni Chimik CuNi44, %
| Ni | Mn | Fe | Si | Cu | Lòt | ROHS Directive | |||
| Cd | Pb | Hg | Cr | ||||||
| 44 | 1% | 0.5 | - | Bal | - | ND | ND | ND | ND |
Pwopriyete mekanik
| Tanperati maksimòm sèvis kontinyèl | 400ºC |
| Rezistans nan 20ºC | 0.49±5%ohm mm2/m |
| Dansite | 8.9 g/cm3 |
| Kondiktivite tèmik | -6 (Max) |
| Pwen k ap fonn | 1280ºC |
| Fòs rupture, N/mm2 rkwit, mou | 340 ~ 535 Mpa |
| Fòs rupture, N/mm3 woule frèt | 680 ~ 1070 Mpa |
| elongasyon (anneal) | 25% (Min) |
| Elongasyon (woule frèt) | ≥Min)2% (Min) |
| EMF vs Cu, μV/ºC (0 ~ 100ºC) | -43 |
| Estrikti mikrografik | ostenit |
| Pwopriyete mayetik | Non |