Lachin Kanthal A/0cr25al5 Fecral Alloy Flat Fil pou fabrikasyon chofaj ak faktori |TANKII

Kanthal A/0cr25al5 Fecral Alloy Flat Fil pou chofaj

Deskripsyon kout:

Modèl NO:Cr25Al5 Fecral alyaj Rod

Sifas:Bright

OEM:WI

Pake transpò:Ka an bwa oswa katon

Orijin:Lachin

Anbalaj:Estanda

Trademark:TANKII

Spesifikasyon:0.1 * 5mm

Kòd HS:7408220000

Pò:Shanghai, Lachin

Kapasite pwodiksyon:2000 tòn / ane

Kondisyon Peman:L/C, T/T, Western Union, Paypal

Klasifikasyon:Fekral

Tanperati itilizasyon ki pi wo a:1250c

Dansite:7.1g/cm3

Rezivite:1.35

Epesè:0.1mm

Lajè:5mm

Voye imèl ba nou

Pwodwi detay

FAQ

Tags pwodwi

0Cr25Al5Tanperati ki wo Rezistans chofajFecral Alloy fil plat

Deskripsyon jeneral
FeCrAl alyaj fèt pa yon wo-tanperati, ferritic fè-chromium-aliminyòm alyaj ki ka itilize nan tanperati jiska 1350degree.Aplikasyon tipik pou0Cr21Al6Nb yo kòm elektrikeleman chofajs nan gwo-tanperati founo nan tretman chalè, seramik, vè, asye, ak endistri elektwonik.

Karakteristik:
Avèk lavi sèvis long.Heating moute vit.Segondè efikasite tèmik.Inifòmite tanperati.Ka itilize vètikal.Lè yo itilize nan vòltaj nominal la, pa gen okenn matyè temèt. Li se yon pwoteksyon anviwònman elektrik chofaj fil elektrik.Ak yon altènativ a koute chè nichrome fil la.Ou ka Customized selon kondisyon kliyan

FeCrAl alyaj yo karakterize pa ekselan rezistans oksidasyon ak trè bon estabilite fòm sa ki lakòz lavi eleman long.

Yo anjeneral yo itilize nan eleman chofaj elektrik nan founo endistriyèl ak aparèy kay.

Fe-Cr-Al alyaj ak rezistans segondè ak tanperati sèvis pase sa pou NiCr alyaj ak tou gen pi ba pri.

Aplikasyon

0Cr21Al6Iron-chrome-aliminyòm rezistans elektrik teren lajman itilize pou fè eleman chofaj elektrik nan aparèy kay ak founo endistriyèl.Aplikasyon tipik yo se fè plat, machin planch, aparèy chofaj dlo, mouri plastik bòdi, fè soude, eleman tubulaires ki kouvri metal ak eleman katouch.

zòn aplikasyon an

Pwodwi nou yo lajman ki itilize nan ekipman tretman chalè, pati oto, fè ak manifakti asye,

endistri aliminyòm, ekipman métallurgique, ekipman pétrochimique, machin vè, machin seramik,

machin manje, machin pharmaceutique, ak endistri jeni pouvwa.

Kontni chimik, %

Materyèl alyaj	Konpozisyon chimik %
	C	P	S	Mn	Si	Cr	Ni	Al	Fe	lòt moun
	max(≤)				Si	Cr	Ni	Al	Fe	lòt moun
1Cr13Al4	0.12	0.025	0.025	0.7	≤1.00	12.5-15.0	-	3.5-4.5	Repoze	-
0Cr15Al5	0.12	0.025	0.025	0.7	≤1.00	14.5-15.5	-	4.5-5.3	Repoze	-
0Cr25Al5	0.06	0.025	0.025	0.7	≤0.60	23.0-26.0	≤0.60	4.5-6.5	Repoze	-
0Cr23Al5	0.06	0.025	0.025	0.7	≤0.60	20.5-23.5	≤0.60	4.2-5.3	Repoze	-
0Cr21Al6	0.06	0.025	0.025	0.7	≤1.00	19.0-22.0	≤0.60	5.0-7.0	Repoze	-
0Cr19Al3	0.06	0.025	0.025	0.7	≤1.00	18.0-21.0	≤0.60	3.0-4.2	Repoze	-
0Cr21Al6Nb	0.05	0.025	0.025	0.7	≤0.60	21.0-23.0	≤0.60	5.0-7.0	Repoze	Nb ajoute0.5
0Cr27Al7Mo2	0.05	0.025	0.025	0.2	≤0.40	26.5-27.8	≤0.60	6.0-7.0	Repoze

Pwensipal karakteristik teknik FeCrAl Alloy:

Mak Pwopriyete		1Cr13Al4	1Cr21Al4	0Cr21Al6	0Cr23Al5	0Cr25Al5	0Cr21Al6Nb	0Cr27Al7Mo2
Gwo eleman chimik%	Cr	12.0-12.5	17.0-21.0	19.0-22.0	20.5-23.5	23.0-26.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	2.0-4.0	5.0-7.0	4.2-5.3	4.5-6.5	5.0-7.0	6.0-7.0
	Fe	Balans	Balans	Balans	Balans	Balans	Balans	Balans
	Re	Apwopriye	Apwopriye	Apwopriye	Apwopriye	Apwopriye	Apwopriye	Apwopriye
							Adisyon Nb:0.5	Adisyon Mo:1.8-2.2
Konpozan max.sèvi ak tanperati		950	1100	1250	1250	1250	1350	1400
Pwen k ap fonn		1450	1500	1500	1500	1500	1510	1510
Dansite g/cm3		7.40	7.35	7.16	7.25	7.10	7.10	7.10
Rezistivite μΩ·m,20		1.25±0.08	1.23±0.06	1.42±0.07	1.35±0.06	1.45±0.07	1.45±0.07	1.53±0.07
Fòs Tensile Mpa		588-735	637-784	637-784	637-784	637-784	637-784	684-784
To ekstansyon%		16	12	12		12	12	10
Frekans koube repete				5	5	5	5	5
Liv rapid h/		-			80/1300	80/1300		50/1350
Espesifik Chalè J/g.		0.490	0.490	0.520	0.460	0.494	0.494	0.494
Koefisyan kondiksyon chalè KJ/Mh		52.7	46.9	63.2	60.1	46.1	46.1	45.2
Koefisyan ekspansyon lineyè aX10-6/ (20-1000)		15.4	13.5	14.7	15.0	16.0	16.0	16.0
Dite HB		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Mikwostrikti		Feritik	Feritik	Feritik	Feritik	Feritik	Feritik	Feritik
Mayetik		Mayetik	Mayetik	Mayetik	Mayetik	Mayetik	Mayetik	Mayetik