Copper Alloy Plak Alloy 25 C17200 Beryllium Copper
Konpozisyon chimik
| Eleman | Eleman |
| Be | 1.85-2.10% |
| Ko+Ni | 0.20% Min |
| Co+Ni+Fe | 0.60% Max. |
| Cu | Balans |
Pwopriyete fizik tipik
| Dansite (g/cm3) | 8.36 |
| Dansite anvan laj redi (g/cm3 | 8.25 |
| Modil elastik (kg/mm2 (103)) | 13.40 |
| Koyefisyan ekspansyon tèmik (20 °C a 200 °C m/m/°C) | 17 x 10-6 |
| Kondiktivite tèmik (kal/(cm-s-°C)) | 0.25 |
| Ranje k ap fonn (°C) | 870-980 |
Pwopriyete mekanik (anvan tretman redi):
| estati | Fòs rupture (Kg/mm3) | Dite (HV) | Konduktivite ( IACS %) | Elongasyon (%) |
| H | 70-85 | 210-240 | 22 | 2-8 |
| 1/2H | 60-71 | 160-210 | 22 | 5-25 |
| 0 | 42-55 | 90-160 | 22 | 35-70 |
Apre tretman redi
| Mak | Fòs rupture (Kg/mm3) | Dite (HV) | Konduktivite (IACS%) | Elongasyon (%) |
| C17200-TM06 | 1070-1210 | 330-390 | ≥17 | ≥4 |
Karakteristik
1. Segondè konduktiviti tèmik
2. Segondè rezistans korozyon, espesyalman apwopriye pou mwazi pwodwi polyoxyethylene (PVC).
3. Segondè dite, mete rezistans ak severite, kòm foure yo itilize ak asye mwazi ak aliminyòm ka fè mwazi an jwe yon trè efikas, prolonje lavi sa a ki sèvis.
4. Polisaj pèfòmans se yon bon bagay, ka reyalize segondè presizyon sifas glas ak konsepsyon fòm konplike.
5. Bon rezistans tackiness, fasil pou soude ak lòt metal, fasil pou D', pa gen okenn bezwen tretman chalè adisyonèl.