Silver Copper Fil AG50cu50 Silver Alloy Fil

Deskripsyon kout:

AG50Cu50, Pwen k ap fonn se 779-850 C

Dyamèt: 0.1mm -3.0mm

AG72Cu28, Pwen k ap fonn se 779-779 C

Dyamèt: 0.08mm-6.0mm

AG45Cu30Zn25, pwen metling la se 660-725 C


  • Modèl NO:Ag50Cu50
  • Gwosè:0.02mm Min.
  • sifas:Bright
  • estanda:GB/ASTM
  • Pwodwi detay

    FAQ

    Tags pwodwi

    Dyamèt: 0.1mm-6.0mmAplikasyon: apwopriye pou brasaj asye, Nerjaveèi asye, alyaj kòb kwiv mete, alyaj nikèl ak elatriye.
    Pake: 1Kg / bobin;1Kg / polybag;2Kg / polybag;Bag, keratin ak flux kouvwi Disponib;Carton oswa selon demann.

    Ajan
    Brazage alyaj
    Konpozisyon chimik
    (%)
    Solidus Likid Spesifikasyon
    (mm)
    Estanda
    BAg10CuZn
    (HL301)
    Ag: 9.0-11.0
    Cu: 52.0-54.0
    Zn:35.0-39.0
    Lòt: Max0.15
    815ºC 850ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    Enterprise
    BAg15CuZn Ag: 14.0-16.0
    Cu:46.0-48.0
    Zn:36.0-40.0
    Lòt: Max0.15
    750ºC 830ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    Enterprise
    BAg18CuZn Ag, Cu, Zn 700ºC 815ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    Enterprise
    BAg20CuZn Ag: 19.0-21.0
    Cu: 43.0-45.0
    Zn:34.0-38.0
    Lòt: Max0.15
    690ºC 810ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    EN1044:1999
    AG206
    BAg25CuZn
    (HL302)
    Ag: 24.0-26.0
    Cu:39.0-41.0
    Zn:33.0-37.0
    Lòt: Max0.15
    700ºC 790ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    EN1044:1999
    AG205
    ISO 17672:2010 Ag225
    BAg30CuZn Ag: 29.0-31.0
    Cu:37.0-39.0
    Zn:30.0-34.0
    Lòt: Max0.15
    680ºC 765ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    SAK-20
    EN1044:1999
    AG204
    ISO 17672:2010 Ag230
    BAg35CuZn Ag: 34.0-36.0
    Cu:31.0-33.0
    Zn:31.0-35.0
    Lòt: Max0.15
    685ºC 775ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    BAg-35
    BAg44CuZn Ag: 43.0-45.0
    Cu:29.0-31.0
    Zn:24.0-28.0
    Lòt: Max0.15
    675ºC 735ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    EN1044:1999
    AG203
    ISO 17672:2010 Ag244
    BAg45CuZn
    (HL303)
    Ag: 44.0-46.0
    Cu:29.0-31.0
    Zn:24.0-27.0
    Lòt: Max0.15
    665ºC 745ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    SAK-5
    BAg50CuZn
    (HL304)
    Ag: 49.0-51.0
    Cu: 33.0-35.0
    Zn:14.0-18.0
    Lòt: Max0.15
    690ºC 775ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    SAK-6
    BAg60CuZn Ag: 59.0-61.0
    Cu: 25.0-27.0
    Zn:12.0-16.0
    Lòt: Max0.15
    695ºC 730ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    EN1044:1999
    AG202
    BAg65CuZn
    (HL306)
    Ag: 64.0-66.0
    Cu:19.0-21.0
    Zn:13.0-17.0
    Lòt: Max0.15
    670ºC 720ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    SAK-9
    BAg70CuZn
    (HL307)
    Ag: 6.0-7.0
    Cu:19.0-21.0
    Zn:8.0-12.0
    Lòt: Max0.15
    690ºC 740ºC Rod / Fil / Bag / Plat
    ≥φ0.2
    Dezabiye / Belt / Foil
    /preforming
    Thickness≥0.05
    2.0≤Width≤100
    GB/T10046-2008
    AWS A5.8
    SAK-10